1.widely used for solar water heater
2.ensure operation in winter
3.15 years' warranty for tube
Port: shanghai/ningbo
Minimum Order Quantity: 300 Piece/Pieces
Supply Ability: 15,000,000 Piece/Pieces per Year
Payment Terms: L/C,T/T
Contact SupplierPackaging Detail: packed by carton with PE fom insinde
Delivery Detail: 7 days after po
Tube structure | Borosilicate 3.3 glass |
External pipe diameter and thickness | Φ=47±0.7mm &=1.6mm Φ=58±0.7mm &=1.6mm Φ=70±0.7mm &=1.6mm |
Internal pipe diameter and thickness | Φ=37±0.7mm &=1.6mm Φ=47±0.7mm &=1.6mm Φ=58±0.7mm &=1.6mm |
Tube lenghth | from 1.2 to 2.1 |
Sediment method | Three Targets magnetron sputtering plating |
Absorptivity | 0.93-0.96 |
Emittance | <=6.0%(75-80°C) |
Stagnation parameter | 240~260 |
Average heat loss | <=0.6 |
Three-target glass solar vacuum tube
1) high cold resistence
2) high heat resistence
3) fast thermal
4) low emission
three-target glass solar vacuum tube
1, Three-target Solar vacuum tube for solar water heater
2, ISO9001,ISO14001, CE certifications
3, 0.91 transmittance of the outer tube
4, 10 to 12 days delivery time
5, five years warranty
Specifications:
1, Vacuum tube is consists of two layer of glass tubes
2, ISO900:2000, CE certificate;
3, 0.91 transmittance of outer tube
4, The outer tube is made of extremely strong transparent quartz sand which can resist impact from hail up to 30mm in diameter.
5, The inner tube is also made of quartz sand, but it is coated with a special selective coating with strong heat absorption and lowest heat loss.
6, The air is evacuated from the space between the two glass tubes to form a vacuum, so it eliminates heat loss.
7, This why the tubes are able to absorb the energy from infrared rays which can pass through clouds.
8, So it also can operate in low temperature and low sunlight medium.
Structure | All-Glass Double Tube Co-Axial Structure |
Glass Material | High Borosilicate 3.3 Glass |
External Pipe Diameter & Thickness | dia.=47±0.5mm &=1.6mm, dia.=58±0.5mm &=1.6mm, dia.=70±0.5mm &=2.0mm, |
Internal PipeDiameter & Thicknessdi | dia.=37±0.5mm &=1.6mm, dia.=47±0.5mm &=1.6mm, dia.=58±0.5mm &=1.6mm, |
Pipe Length | 1500mm, , 1800mm |
Absorptive Coating PropertyStructure | Cu/SS-ALN(H)/SS-ALN(L)/ALN |
Sediment Method | Three Layer Magnetron Sputtering Plating |
Specific Absorptionas | 0.92~0.96(AM1.5) |
Emission Ratio | 0.01~0.03(80°C±5°C) |
Vacuum | P≤2.0×10-3Pa |
Idle Sunning Property | Y= 260 ~ 300m²°C/KW |
Solar Irradiation for Obtaining a Preset Water Temperature | H≤4.7 MJ/m²(dia.58)H=3.7~4.2 MJ/ m² H≤3.7 MJ/ m²(dia.47)H=2.9~3.2 MJ/ m² |
Average Heat Loss Coefficient | Ult=0.4~0.6W/( m².°C) |
Pressure-Endure Ability | 0.6Mpa |
Hail-Endure Ability | 30mm |
Lifetime | more than 15years |