1.The General Description
MoSi2 heating elements are resistive heating elements based on molybdenum disilicide. The molybdenum disilicide heating elements prevents the inner core from oxidation by forming a compact quartz glass coating at the surface under high temperature. The temperature generated by MoSi2 goes as high as 1700~1800°C in oxidation atmosphere. They can be widely used in such applications as sintering and heat treatment on electronic ceramics, structural ceramics, magnetic materials, flameproof materials, glass, metallurgy, etc. The resistance of the heating elements is independent on their mission time. The MoSi2 heating elements hardly age, which allows the mixed use of new and old packages.
2. The Species of Yuhao MoSi2 heating elements
Dimension marks of elements:
diameter:D1/D2,mm/mm Hot zone length: Le, mm
Cold end length: Lu, mm Shank spacing: A, mm
Examples:
1) U shape,
D1=3mm,D2=6mm,Le=140mm,LU=125mm,A=25mm
specify as : YuhaoU Shape,3/6×140×125×25
2) W Shape
D1=6mm,D2=12mm,Le=300mm,Lu=250mm,A=50m
specify as : Yuhao W Shape 6/12×300×250×50
3. Physical and Chemical Properties of Elements
1) Physical property
Volume density | 5.5~5.6kg/cm3 | Bend strength | 515~25kg/cm2 |
Vickers-hardness | (HV)570kg/mm2 | Porosity rate | 7.4% |
Water absorption | 1.2% | Hot extensibility | 4% |
2) Chemical property
Oxygen-resistance under high temperature: in oxidizing atmosphere,on the surface of element owing to the high-temperature combustion a layer of compact quartz(sio2)protective film is formed to prevent Mosi2 from continuously oxidizing.When the element temperature is higher than 1700°C,the sio2 protective film, Whose fusing point is 1710°C, is fused,and the sio2 is fused into molten drops owing to the action of its surface extension, so that loses its protective ability,In the oxidizing atmosphere,when the element is continuously used,again the protective film forms.
It should be pointed out that element cannot be used for rather long time in 400-700°C,or it will be powdered owing to the strong oxidizing action in low temperature.
4. Installation of Elements
1)Vertically hanging
Under normal temperature, MoSi2 element is very brittleness,while under high temperature it is plasticity.So,the better way for installation if the U Shape element is to hang it vertically,to the furnace top through the support clamping chuck H.The aim of such way is to avoid putting the mechanical stress directly to the element heat-generating end ,or the element will easily be broken.
2)Support clamp
Support clamp are applied to 9/18 and 6/12 two kinds of elements respectively. the support clamp supports the whole weight of the element and the position of the element is also determined by it .therefore ,it must be installed carefully to assure that the element it vertically hung.in order to prevent the element from being over heated locally,the taper part of the element lower end must put into the furnace chamber.
3)Wire clip
The wire connection clamp connecting MoSi2 element is made of aluminum woven wire or multilayer aluminum foil.the steel plate outside it only acts as a clamp and isn't used for electric conduction.For 6/12 element,single rowing wire is used ,and for 9/18element,double-rowing wire is used ,the end of the lead wire should be a little larger than the linear distance between the element and bus.
Look forward yo your enqury!